Sand and gravel aggregate is a collective name for materials such as sand, gravel, crushed stone, block stone, and dressed stone. It is a basic material for the production of concrete, mortar, asphalt mixture, إلخ., and is mainly used for infrastructure construction such as high-rise buildings, الطرق السريعة, السكك الحديدية, الجسور, الهندسة البلدية, water conservancy projects, المطارات, and wharfs.

Aggregate with a particle size larger than 5mm is called coarse aggregate, which is what we often call stone. Aggregate with a particle size of less than 5mm is called fine aggregate, also known as sand.

هذه المقالة تلخص 15 في كثير من الأحيان أسئلة حول مجاميع الرمال والحصى. آمل أن نتمكن من تقديم بعض المساعدة في البناء.

س: What systems are generally composed of sand and gravel aggregate production lines?

أ: It mainly includes four systems:

نظام التغذية: عمومًا, a vibrating feeder is used to be responsible for the supply of stone;

Transportation system: The belt conveyor is responsible for the transportation of materials between different equipment;

Crushing system: This is the core of the entire production line, which generally consists of multiple crushers. Its function is to crush various ore raw materials to the required particle size;

Screening system: It includes circular vibrating screen and linear vibrating screen.

س: What is aggregate gradation?

أ: Aggregate gradation is the proportional relationship between the particles of different particle sizes that make up the sand and gravel aggregate. That is to say, the aggregate contains the proportion of particles with different thicknesses, which is an indicator to measure the thickness of the aggregate.

Different sands have different gradations. The smaller the particle size and the larger the proportion, the finer the sand. Conversely, the larger the proportion of particles with larger particle sizes, the coarser the sand. The same is true for stones.

س: What are the mud content, stone powder content and clay lump content?

أ: Mud content refers to the content of particles with a particle size of less than 75μm in natural sand;

The stone powder content refers to the content of particles with a particle size of less than 75μm in artificial sand;

The content of clay lumps refers to the content of particles in the sand whose original particle size is greater than 1.18mm and less than 600μm after being immersed in water and kneaded by hand.

س: What is the particle gradation and fineness of sand? What effect do they have?

أ: Particle gradation: This refers to the situation where sands of different particle sizes are matched with each other. If the particle gradation is poor and the void rate is large, more cement paste is needed to fill. على العكس تماما, if the particle gradation is good and the void rate is small, less cement paste filling is required.

The thickness of the sand: This refers to the average thickness of sand of different particle sizes when mixed together. Under the conditions of the same amount of sand, the surface area of coarse particles is small, and the surface area of fine particles is large, and the amount of cement paste used to wrap the particles will be different.

It was found that when mixing concrete, the thickness and particle gradation of sand should be considered at the same time. When the sand contains more coarse particles, moderately medium particles and a small amount of fine particles, there is both a smaller void rate and a smaller total surface area. فضلاً عن ذلك, this not only reduces the amount of cement, but also improves the compactness and strength of the concrete.

س: What matters should be paid attention to when coarse and fine aggregates enter the production site?

أ: Coarse aggregate should mainly control its particle size, gradation, particle shape, stone powder content, and clay lump content.

Fine aggregate should control fineness modulus, mud content and clay lump content.

فضلاً عن ذلك, no matter coarse aggregate or fine aggregate, macro inspection should be carried out for each vehicle, and unqualified vehicles shall not be unloaded. فضلاً عن ذلك, according to the requirements of the specification, the indicators should be inspected in batches.

س: What are the characteristics of river sand? Why are mountain sand, sea sand and desert sand not suitable for construction sand?

أ: River sand has the advantages of good grain shape, firmness, durability, abundant resources, low mining cost and less impurities.

Mountain sand is easily weathered, with rough surface, many edges and corners, many impurities and large mud content.

Although sea sand is rich in resources, it has many impurities and chloride ions, which is corrosive and has high desalination costs.

Desert sand is too fine, contains a lot of soil, is too sticky, and has poor plasticity.

لذلك, mountain sand, sea sand and desert sand cannot be used as construction sand.

س: How to distinguish artificial sand and river sand from the appearance?

أ: Artificial sand is the sand and gravel aggregate obtained after being crushed by sand making machine such as vertical shaft impact crusher. Compared with natural river sand, it has the characteristics of sharp edges and corners, many needles and roughness.

River sand is dug directly from the river, so it will be mixed with small pebbles and fine sand.

The river sand is eroded by the river water for a long time, and the edges and corners are relatively rounded. The edges and corners of the artificial sand produced by the sand and gravel equipment are relatively sharp and distinct.

س: ما هي أنواع الرمال التي يمكن تصنيفها وفقًا للمتطلبات الفنية?

أ: الرمال مقسمة إلى الفصل الأول, الفئة الثانية والفئة الثالثة وفقًا للمتطلبات الفنية:

الفئة الأولى مناسبة للخرسانة مع درجة القوة أكبر من C60;

الفئة الثانية مناسبة للخرسانة مع درجات القوة بين C30 و C60 ومقاومة الصقيع, عدم وجود متطلبات أو متطلبات أخرى;

الفئة الثالثة مناسبة للخرسانة وبناء الهاون مع درجة القوة أقل من C30.

س: ما هو دور الرمال والحصى في الإنتاج الخرساني?

أ: يمكن أن يوفر إجمالي الرمال والحصى استقرارًا جيدًا, ارتداء المقاومة والمتانة للخرسانة. علاوة على ذلك, يمكن أن تلعب أيضًا دور تقليل الانكماش, تثبيط انتشار الكراك, وتقليل حرارة الترطيب. يمكن أن تؤدي إضافة أكبر قدر ممكن من الإجمالي إلى الخرسانة إلى تقليل تكلفة الخرسانة دون التأثير على خصائصها.

س: إذا كانت الرمال جيدة جدًا, ما هو التأثير على الخرسانة? ماذا لو كانت الرمال الجميلة متوفرة فقط?

أ: إذا كانت الرمال جيدة جدًا, يرتفع الطلب على المياه للخرسانة. فضلاً عن ذلك, الخرسانة المحضرة بالرمل الناعم لها قابلية للضخ واللدونة الضعيفة, وسوف تنخفض قوة الخرسانة, ومن السهل الكراك.

إذا كان هناك فقط رمل ناعم في مصدر الرمال, يمكن تحضير الخرسانة المسلحة عن طريق إضافة بعض الرمال المصنوعة من الآلة مع الرمل الناعم. على سبيل المثال, رمل ناعم مع معامل الدقة أقل من 2.0 يمكن خلطها مع الرمال الصنع مع معامل الدقة من 3.0 ل 3.2. النسبة بين الاثنين حول 6 ل 4, ثم راقب سيولة وقابلية الضخ. يمكن تحديد النسبة المحددة عن طريق التجربة.

س: إذا كانت الرمال تحتوي على الكثير من الطين, أو حتى لديها كتل الطين, هل سيكون لها تأثير كبير على الخرسانة?

أ: هذا له تأثير على الخرسانة. إذا كانت الرمال تحتوي على كمية كبيرة من الطين, سيكون الطلب على المياه للخرسانة كبيرة, ستكون اللدونة سيئة, سوف يزيد الانكماش, ستنخفض قوة الخرسانة, وسيكون الهيكل سهل الكراك. لذلك, من الضروري التحكم في محتوى الطين من الرمال ليكون أقل من أو يساوي 3% (C30 ~ C50), ويجب أن يكون محتوى الطين من الخرسانة عالية القوة أقل.

أما بالنسبة لكتلات الطين, بالإضافة إلى الآثار المذكورة أعلاه, كما سيؤثر بشكل خطير على قوة الملموسة. على سبيل المثال, يمكن أن تضعف كتل الطين مقاطع خرسانية, تطفو عند سكب الأرض, وتشكيل الحفر على السطح بعد تقلص.

س: What is the appropriate amount of stone powder in concrete?

أ: Adding stone powder to concrete is beneficial. لكن, the stone powder content should be appropriate.

The main component of stone powder in machine-made sand is calcium carbonate, but the hydration is not unlimited, and it is also limited by the composition of cement.

If the content of stone powder is too high, it is not conducive to the bonding of sand aggregate and cement, which will reduce the performance of concrete. فضلاً عن ذلك, when the stone powder content exceeds the limit, it is not conducive to the durability of concrete. This is because the water retention capacity of stone powder is obviously reduced, and the drying shrinkage is significantly larger.

Experiments show that generally, يجب التحكم في محتوى مسحوق الحجر في الخرسانة أدناه C50 10% ل 15%, في حين يجب ألا يتجاوز محتوى مسحوق الحجر في الخرسانة فوق C50 10%.

س: لماذا هي قوة الخرسانة الملموسة 3 ~ 4MPa أقل من تلك الموجودة في الخرسانة الحجرية المسلحة لنفس نسبة الخرسانة?

أ: السطح الخشن للركام الخشن مفيد لتعزيز قوة الواجهة بين معجون الأسمنت والكلي.

وفقا للاختبار, من ناحية, تحتوي الخرسانة المحضرة بالحصى على المزيد من الحجر المتجول, ومؤشر التكسير أقل من تلك الموجودة في الحجر المكسور. علاوة على ذلك, سطحه سلس وقوة الواجهة منخفضة, لذا فإن قوة الخرسانة التي أعدت من قبلها ستكون أقل من 3 ~ 4MPa.

س: ما هو رد فعل القلويات? ما هو التأثير?

أ: القلويات (Na2O, Ka2O) في الخرسانة يتفاعل كيميائيًا مع الإجمالي الذي يكون تركيبه الكيميائي نشطًا سيليكا نشطة لتشكيل هلام قلوية-ثم تمتص الماء ويتوسع, ويؤدي إجهاد التوسع إلى كسر الخرسانة. وتسمى هذه العملية رد فعل القلويات. سيؤدي هذا التفاعل إلى توسع الحجم المحلي داخل الخرسانة, وحتى تسبب في أن يكون للبنية الخرسانية فشل واسع.

س: كيفية منع رد فعل القلويات?

أ: إذا كان الركام الخشن المحلي يحتوي على السيليكا النشطة, يجب أن يكون المحتوى القلوي للخلط الملموس محدودًا تمامًا. عند استخدام المجاميع القلوية, يجب أن يكون المحتوى القلوي الكلي لمختلف المواد في الخرسانة أقل من أو يساوي 3% من الكتلة الملموسة.